A laboratory study evaluated the influence of a dentin desensitizer (D/Sense 2) on the microtensile bond strength of two adhesive systems: a self-etching primer (Bistite II SC) and a one-bottle adhesive (Prime & Bond 2.1). Sixteen crown dentin discs were obtained from extracted sound human third molars. Dentin surfaces were ground with 600 grit silicon carbide (SiC) abrasive papers to produce a standardized smear layer. Teeth were randomly divided into four groups (n=4). G1-D/Sense 2 + Prime & Bond 2.1; G2-D/Sense 2 + Bistite II SC; G3- and G4-dentin surfaces were bonded with Prime & Bond 2.1 and Bistite II SC, respectively, with no previous treatment with D/Sense 2. Eight mm high resin composite crowns (TPH Spectrum) were incrementally built-up on the treated surfaces. One sample from each group was prepared for evaluation of the hybrid layer on SEM. The specimens for the microtensile test were serially sectioned perpendicular to the adhesive layer to obtain 1 mm2 bounded sticks. Then, each stick was submitted to the microtensile test performed at a 0.5 mm/min crosshead speed. One-way ANOVA and Tukey test showed statistically significant differences among the groups (p<0.05). Values in MPa were: G1-17.85; G2-9.88; G3-35.16; G4-15.57. Based on the results of this study, it can be concluded that the D/Sense 2 desensitizer decreased the bond strength of Prime & Bond 2.1 and Bistite II SC bonding systems.
 ...
PMID:The influence of a dentin desensitizer on the microtensile bond strength of two bonding systems. 1193 6

This study evaluated the microtensile bond strength (pTBS) of ethanol/water- and acetone-based, one-bottle adhesive systems to enamel (E) and dentin (D) in the presence (P) or absence (A) of their respective solvents. Thirty-two freshly extracted third molars were flattened with 600-grit SiC paper and restored with Single Bond (SB) or Prime&Bond 2.1 (PB) according to the manufacturers' instructions and after full solvent elimination. The molars were divided into eight test groups (n = 4): G1-SB-E-P, G2-SB-E-A, G3-PBE-P, G4-PB-E-A, G5-SB-D-P, G6-SB-D-A, G7-PB-D-P and G8-PB-D-A. After applying the adhesive resins, composite crowns of approximately 8 mm were built up with TPH Spectrum composite. After 24-hour water storage, the specimens were serially sectioned bucco-lingually to obtain 0.8 mm slabs that were trimmed to an hourglass shape, approximately 0.8 mm2 at the bonded interface. The specimens were tested in tension using a universal testing machine (0.5 mm/minute). The results were statistically analyzed by ANOVA and Tukey test. The frequency of fracture mode was compared using the Kruskal-Wallis test. There were no statistically significant differences in mean bond strength among the groups restored with or without solvent for enamel. However, the results were significantly different for the dentin groups (MPa): G5-26.2 +/- 8.6a; G7-23.6 +/- 11.3ab; G6-12.8 +/- 2.1bc; G8-6.2 +/- 3.1c. SEM examination indicated that the dentin group failure modes were significantly different from the enamel groups. The results suggest that the presence of organic solvents does not influence microTBS to enamel. However, microTBS to dentin was significantly affected by the absence of solvents in the adhesive system.
 ...
PMID:The effect of organic solvents on one-bottle adhesives' bond strength to enamel and dentin. 1465 83

This study tested the effects of long-term storage and aluminum oxide air abrasion on the bond strength of self-etching adhesive systems. Extracted human third molars were ground flat with 600-grit SiC paper to expose middle coronal dentin. Clearfil SE Bond and One-Up Bond F were applied to dentin surfaces in accordance with manufacturers instructions with or without previous aluminum oxide 50 microm air abrasion. A crown was built up with the resin composite TPH Spectrum and the specimens were stored in water for 24 hours. The bonded assemblies were vertically sectioned into beams for microtensile bond testing. The beams of each tooth were individually immersed in bottles containing water at 37 degrees C for one day, three and six months; the water was changed daily. The specimens were then subjected to microtensile bond testing. The bond strength data were subjected to ANOVA and Tukey Kramer test. Fractured specimens were analyzed in a scanning electron microscope to determine failure modes. Air abrasion improved Clearfil SE Bond bond strength in the three month evaluation. No significant difference was found between the two adhesives systems, but bond strengths gradually decreased over time. Failure modes varied significantly among groups and were influenced by long-term storage and aluminum oxide air abrasion.
 ...
PMID:Influence of air abrasion and long-term storage on the bond strength of self-etching adhesives to dentin. 1755 72

This study evaluated the influence of the method and period of storage on the adhesive bond strength of indirect composite resin to bovine dentin. Ninety bovine incisors were stored in three different solutions: 0.2% thymol, 10% formalin, and 0.2% sodium azide, during 3 periods of storage: 7 days, 30 days and 6 months, resulting in 9 groups (n = 10). The roots were cut off and the buccal surface was ground with #600-grit silicon carbide paper. The surface was conditioned with 37% phosphoric acid for 15 s and a composite resin restoration (TPH Spectrum) was fixed using a one-bottle adhesive system (Adper Single Bond) and a dual-cured resinous cement (Rely X ARC) under a load of 500 g for 5 minutes. The samples were serially cut perpendicular to the bonded interface to obtain slices of 1.2 mm in thickness. Each slab was trimmed with a cylindrical diamond bur resulting in an hourglass shape with a cross-sectional area of approximately 1 mm(2). The microtensile bond strength (microTBS) testing was performed in a testing machine (EMIC 2000 DL) at a 0.5 mm/minute crosshead-speed until failure. After fracture, the specimens were examined under SEM to analyze the mode of fracture. muTBS Means were expressed in MPa and the data were analyzed by two-way ANOVA (3X3) and the Tukey test (alpha = 0.05). The storage times of 7 and 30 days produced no significant difference irrespective of the solution type. The formalin and thymol solutions, however, did have a negative influence on bond strength when the teeth were stored for 6 months.
 ...
PMID:Influence of method and period of storage on the microtensile bond strength of indirect composite resin restorations to dentine. 1914 92

To determine the shear bond strength of 10 self-etching adhesive systems to dentin and enamel, flat bonding sites were prepared on 216 extracted human molar teeth, using 600-grit silicon carbide paper to expose dentin or enamel. Following the application of each adhesive system, bonded assemblies of Spectrum TPH were prepared using a gelatin capsule matrix (n = 24). After 24 hours of storage in water at 37 degrees C, 12 specimens from each enamel and dentin group were debonded. This was followed by thermocycling for 6,000 cycles between water baths at 5 degrees C and 55 degrees C, with a dwell time of 20 seconds in each bath. Specimens were loaded to failure in a testing machine with a crosshead speed of 5 mm/minute. Statistical analysis included a one-way ANOVA and least square difference post hoc test. There were significant differences in shear bond strength for both enamel and dentin among the materials tested (p < 0.05).
 ...
PMID:Bond strength of composite to dentin and enamel using self-etching adhesive systems. 1981 15

This study examined the effect of different light activation modes for light-cured resin-based composites on the shear bond strength to dentin of two one-bottle adhesives with differing acidity. In this experimental study, a flat middle dentin surface was prepared on 110 extracted sound molars using a 600-grit polish paper. The teeth were then randomly divided into 10 equal groups (n = 11). One-Step Plus (OS) and Prime & Bond NT (P&B NT) were used according to the manufacturer's instruction with their respective composite (Aelite, Spectrum TPH) applied and cured using five different light-activation modes: 1. Conventional (CO): 600 mW/cm2 (40 seconds) 2. Soft-Start I (SSI): 100 mW/cm2 (10 seconds) 600 mW/cm2 (30 seconds) 3. Soft-Start II (SSII): 200 mW/cm2 (10 seconds), 600 mW/cm2 (30 seconds) 4. Pulse-Delay I (PDI): 100 mW/cm2 (3 seconds), 3-minute delay, 600 mW/cm2 (37 seconds) 5. Pulse-Delay II (PDII): 200 mW/cm2 (3 seconds), 3-minute delay, 600 mW/cm2 (37 seconds) After 24 hours storage in distilled water at room temperature, a shear bond strength (SBS) test was performed using an Instron machine at 1 mm/minute and the results were recorded in MPa. Statistical analysis included two-way ANOVA and Tukey HSD (p < 0.05). The highest SBS (MPa) was shown in the OS conventional group (19.62 +/- 2.21) and the lowest SBS was shown in P&B NT, PDII (5.93 +/- 1.79). In each group of five curing modes, the mean SBS for P&B NT was significantly lower than OS: conventional mode--P&B NT (17.27 +/- 1.98) vs OS (19.62 +/- 2.21); SSI-P&B NT (10.84 +/- 2.82) vs OS (13.09 +/- 1.24); SSII - P&B NT (14.78 +/- 1.63) vs OS (18.79 +/- 1.57); PDI-P&B NT (5.93 +/- 1.79) vs OS (11.97 +/- 2.59) and PDII-P&B NT (11.82 +/- 1.24) vs OS (16.00 +/- 1.62) (p < 0.001 for all comparisons). For each of the adhesives, the ranking of SBS was as follows: CO > SSII > PDII > SSI > PDI, with the two-paired comparisons of curing modes being significantly different (p < 0.05). The results of the current study indicated that the bond strength of P&B NT might be compromised by the higher acidity of this adhesive compared to OS during each curing mode, especially PDI. The conventional mode was least affected by the acidity of the adhesive.
 ...
PMID:Effect of light activation mode on the incompatibility between one-bottle adhesives and light-cured composites: an in vitro shear bond strength study. 1983 Sep 70