Gene/Protein Disease Symptom Drug Enzyme Compound
Pivot Concepts:   Target Concepts:
Query: UMLS:C0015672 (fatigue)
 51,768 document(s) hit in 31,850,051 MEDLINE articles (0.00 seconds)

Bioprosthetic heart valves fail as the result of two simultaneous processes: structural deterioration and calcification. Leaflet deterioration and perforation have been correlated with regions of highest stress in the tissue. The failures have long been assumed to be due to simple mechanical fatigue of the collagen fibre architecture; however, we have hypothesized that local stresses-and particularly dynamic stresses-accelerate local proteolysis, leading to tissue failure. This study addresses that hypothesis. Using a novel, custom-built microtensile culture system, strips of bovine pericardium were subjected to static and dynamic loads while being exposed to solutions of microbial collagenase or trypsin (a non-specific proteolytic enzyme). The time to extend to 30% strain (defined here as time to failure) was recorded. After failure, the percentage of collagen solubilized was calculated based on the amount of hydroxyproline present in solution. All data were analyzed by analysis of variance (ANOVA). In collagenase, exposure to static load significantly decreased the time to failure (P < 0.002) due to increased mean rate of collagen solubilization. Importantly, specimens exposed to collagenase and dynamic load failed faster than those exposed to collagenase under the same average static load (P = 0.02). In trypsin, by contrast, static load never led to failure and produced only minimal degradation. Under dynamic load, however, specimens exposed to collagenase, trypsin, and even Tris/CaCl2 buffer solution, all failed. Only samples exposed to Hanks' physiological solution did not fail. Failure of the specimens exposed to trypsin and Tris/CaCl2 suggests that the non-collagenous components and the calcium-dependent proteolytic enzymes present in pericardial tissue may play roles in the pathogenesis of bioprosthetic heart valve degeneration.
 ...
PMID:Mechanical loading of bovine pericardium accelerates enzymatic degradation. 1038 30

Mechanical loading contributes to the structural deterioration of bioprosthetic heart valves. The influence of stress state during fixation may play a substantial role in their failure, linking fatigue damage caused by buckling and tension and the enzymatic degradation of glutaraldehyde-crosslinked collagen. Bovine pericardia were obtained immediately postmortem and 100 mm x 15 mm samples were cut in the base-to-apex direction. Half the samples were subjected to a uniaxial tensile stress of 250 kPa and half remained unloaded during a crosslinking treatment in 0.5% glutaraldehyde. Tissue samples were rinsed and cut into 16 mm x 4 mm test strips. Half of these strips were exposed to cyclic compressive buckling and alternating tension at 30 Hz for 20 million cycles (approx. 7.5 days) using a custom-built multi-sample fatigue system. Fatigue-damaged and non-damaged samples were subsequently incubated at 37 C for 48 hrs in: (i) Type I bacterial collagenase (20 U/ml) buffered in 0.05 M Tris, 10 mM CaCl2 2H2O (pH 7.4) or (ii) 0.05 M Tris buffer (pH 7.4) only. In both cases, the samples were loaded sinusoidally between 40 and 80 g using a previously described microtensile culture system. Tissue removed from the bath was rinsed in 0.1 M EDTA solution and mounted in a servo-hydraulic mechanical testing system (MTS). Ultimate tensile strength (UTS), maximum tissue modulus, and fracture strain were determined. The percent collagen solubilized was assessed by a colourmetric hydroxyproline assay of the enzyme bath and tissue sample. All data were analyzed by analysis of variance (ANOVA). The results confirmed the synergy between fatigue damage and collagenase proteolysis in these materials; however, there were no significant differences in this effect between simple fixation and stress-fixation up to 20 million cycles. There were significant decreases in the mechanical properties and an increase in the amount of collagen solubilized with increased exposure to fatigue cycling.
 ...
PMID:Stress state during fixation determines susceptibility to fatigue-linked biodegradation in bioprosthetic heart valve materials. 1208 92

Boron removal from wastewaters by electrocoagulation using aluminum electrode material was investigated in this paper. Several working parameters, such as pH, current density, boron concentration and type and concentration of supporting electrolyte were studied in an attempt to achieve a higher removal capacity. The experiments were carried out by keeping the pH of solution constant and optimum pH of solution was determined 8.0 for the aluminum electrode. Although energy consumption increased with decreasing boron concentration, which conductivity of these solutions were low, boron removal efficiency was higher at 100 mg/L than that of 1000 mg/L. Current density was an important parameter affecting removal efficiency. Boron removal efficiency and energy consumption increased with increasing current density from 1.2 to 6.0 mA/cm2. The types of different supporting electrolyte were experimented in order to investigate to this parameter effect on boron removal. The highest boron removal efficiency, 97%, was found by CaCl2. Added CaCl2 increased more the conductivity of solution according to other supporting electrolytes, but decreased energy consumption. The results showed to have a high effectiveness of the electrocoagulation method in removing boron from aqueous solutions.
 ...
PMID:The investigation of parameters affecting boron removal by electrocoagulation method. 1598 28