We synthesized 4-methacryloxyethyl trimellite acid (4-MET) and anhydride (4-META), and tried them as a reactive comonomer for adhesives to bovine enamel. In the case of non-etched enamel, tensile adhesive strength was 40-50 Kg/cm2 after one day immersion in 37 degrees C water, but it decreased below 10 Kg/cm2 after a month immersion in 37 degrees C water. It could be concluded that this adhesion was not sufficient for practical usage. Then we applied this method to an etched enamel. After a series of experiments we concluded that it was necessary to etch bovine enamel surface with 30% citric acid for practical usage. Adhesion of some dental alloys with a PMMA rod was also studied and adhesive strength in Co-Cr alloy was over 150 Kg/cm2 either after one month immersion in 37 degrees C water or 60 times thermal cycles between 4 degrees C and 60 degrees C.
 ...
PMID:[Studies on dental self-curing resins. (17). Adhesion of PMMA with bovine enamel or dental alloys (author's transl)]. 28 86

A new, simple method of modifying the adherend metal surface by a liquid Ga-Sn alloy (Adlloy) was applied to dental precious and base-metal alloys for adhesion with 4-META adhesive resin. Adhesions of 4-META resin to three other surface states--as-polished, oxidized at high temperature, and electroplated tin--were also performed for comparison with the adhesion on Adlloy-modified surfaces. Bond strength measurements were made, and the durability against water at the adhering interface was evaluated. The Adlloy-modified gold alloys (Type IV and 14 K) and silver-based alloys (Ag-Pd and Ag-Cu) showed not only high bond strengths but also excellent water durability at the adhesion interface. Surface modification by Adlloy, however, did not affect adhesion to Ag-In-Zn and base-metal (SUS, Co-Cr, and Ni-Cr) alloys. Adhesion to the tin-electroplated specimens was comparable with that to the Adlloy-modified specimens.
 ...
PMID:A new method for promoting adhesion between precious metal alloys and dental adhesives. 161 83

Adhesion durability between dentin pretreated with 10-3 and 4-META/MMA-TBB resin was studied. Reduction of etching periods with 10-3 was not so effective as expected. The weakening of bond strength during immersion in water at 37 degrees C to the dentin pretreated for 1 sec occurred faster than those for either 5 sec or 10 sec. The strength decreased from 12 MPa at 1 day to 9 MPa at 3 months, 3 MPa at 6 months and finally 2 MPa at 1 year in the case of 1 sec pretreated dentin. On the other hand, the strength became half after the storage in water for 1 year in the cases of 5 and 10 sec pretreated dentins. Combination of 10-3 pretreatment and subsequent glutaraldehyde treatment could stabilize the decrease but not completely. SEM and TEM examinations suggested that dentinal collagen exposed by the etching but not entangled and impregnated by poly (4-META-co-MMA) easily deteriorated by water during the longer immersion. Collagen modified with 10-3 and then with glutaraldehyde was also changed by the longer immersion.
 ...
PMID:[Durability of bonding between 4-META/MMA-TBB resin to dentin pretreated with 10-3. The effect of 10-3 pretreating period and subsequent glutaraldehyde treatment]. 213 46

Adhesion of 4-META to Au-In alloy was improved by adding In equivalent to .15% of Au content. On the basis of the results of Au-In alloys analyzed by XPS, the present study investigated the reason why adhesion of the Au-In alloy was improved. The O 1s spectrum could be separated into three oxygen chemical states, In2O3, chemisorbed H2O, and physisorbed H2O. The amount of chemisorbed H2O decreased remarkably with increasing amount of In. It is considered that the poor adhesive ability of the pure gold and alloys containing only small amounts of In was due to the chemisorbed H2O molecules and insufficient indium oxide on the alloy surface. It was established that excellent adhesion requires an oxide with chemical affinity for 4-META to cover at least 50% of the alloy surface.
 ...
PMID:Adhesion of adhesive resin to dental precious metal alloys. Part II. The relationship between surface structure of Au-In alloys and adhesive ability with 4-META resin. 1021 42